Products

Refractory Bricks

Alumina Silica Fire Brick

High Alumina Brick
Silica Fire Brick
Corundum Brick
Fire Clay Brick

High Alumina Brick

Al2O3: 55-80%;
Refractoriness Under Load: 1420-1530℃;
Cold crushing strength: 40-70MPa;
Standard Size: 230*114*65mm;

High Alumina Refractory Balls

Color: Yellow;
Max service temp: 1800℃;
Al2O3: Max service can up to 95%;
Sample: available;

Curved Fire Bricks

Apparent Porosity, %: ≤26;
Cold Crushing Strength, MPa: ≥40;
Price: Low Ex-factory Price;
Sample: available;

Fused Magnesia Brick

MgO Chemical composition :≥95 ％;
Apparent Porosity :≤18 ％;
Bulk Density/ (g/cm³): 2.31-2.4
Bending strength/ (MPa): ≥58.80

MgO% (≥): 89-97.5
Bulk Density (g/cm³): 2.85-3.0
Refractoriness Under Load (℃): 1500-1700
Size: 230*114*65mm; Customized Sizes

Magnesia Carbon Bricks

MgO%: 69-85
C%: 5-18
Bulk Density (g/cm³): 2.79-3.05
Sample: available;

Magnesia Chrome Brick

MgO%(≥): 45-65
Cr2O3%(≥): 8-16
Apparent Porosity/%(≤): 19-21
Cold Crushing Strength (MPa): 20-35

Magnesia Zirconia Brick

MgO% ≥：70/75/80 ZrO2 %≥：8/10/13;
Apparent Porosity%≤：19;
Bulk Density (g/cm3)≥：2.95;
Refractoriness Under Load:≥1600 °C

Mullite Refractory Brick

Al2O3% (≥): 62-70
Fe2O3)/%(≤): 1.5-1.8
Refractoriness Under Load (℃)(≥): 1760-1780
Sample: available;

Corundum Mullite Brick

Max service temp: 1700℃;
More than 85% Al2O3 and 0.45% Fe2O3;
Color: White;
More than 55MPa cold crushing strength;

Zircon Mullite Brick

Bulk density g/cm3:≥ 3.15;
Cold Crushing Strength (Mpa)≥90;
Apparent Porosity (%)：≤17;
Size: 230*114*65mm; Customized Sizes

SK Fireclay Bricks

Al2O3:≥30-70%;
Bulk Density: 1.9-2.35g/cm³
Refractoriness Under Load: 1250-1480ºC;
Sample: available;

Zircon Refractory Brick

ZrSiO4: ≥15-65%;
Bulk Density: 2.7-3.7g/cm³;
Refractoriness Under Load: 1550-1650ºC;
Cold Crushing Strength: ≥100MPa;

ZrO2%: ≥ 16
Fe2O3%: ≤ 0.5
Bulk Density (g/cm³): ≥ 2.70
Cold Crushing Strength/MPa: ≥ 70

Zirconia Corundum Bricks

Apparent porosity %: ≤20
Refractoriness under load°C: ≥1650℃
Al2O3: ≥45%
Bulk density g/cm3: ≥3.2

Zircon Mullite Brick

Bulk density g/cm3:≥ 3.15;
Cold Crushing Strength (Mpa)≥90;
Apparent Porosity (%)：≤17;
Size: 230*114*65mm; Customized Sizes

Magnesia Spinel Brick

MgO/%(≥): 80
Al2O3/%(≥): 10
Bulk Density (g/cm³)(≥): 2.90
Cold Crushing Strength(≥): 50MPa

Magnesia Alumina Spinel Brick

MgO/%(≥): 80
Al2O3/%(≥): 10
Certification: ISO9001/ISO14001 /ISO45001/ISO50001

Magnesia Iron Spinel Brick

MgO/%(≥): 80
Al2O3/%(≥): 10
Bulk Density (g/cm³)(≥): 2.90
Size: 230*114*65mm; Customized Sizes

Al2O3/%: 95-98
SiO2/%: 0.15-0.5
Fe2O3/%: 0.1-0.3
Refractoriness Under Load: 1700MPa

Cr2O3 %≥：50-93;
Apparent Porosity %：≤16;
Bulk Density g/cm3≥：3.5-4.25;
Load softening temperature, 0.2MPa 0.6%：≥1700;

Chrome Corundum Brick

Bulk density g/cm3: ≥3.25;
Apparent Porosity %: ≤15;
Pressure strength（Mpa）≥1800;
Load softening temperature(0.2Mpa T0.6 ℃): ≥168;

Bulk density g/cm3: ≥1.7
Compressive strength / Mpa: ≥36
Oxidation rate /%: ≤8
Average pore size: ≤0.1

SiO2%: ≥94
Fe2O3/%: ≤1.4
True Density (g/cm³): ≤2.35
Refractoriness Under Load (℃): ≥1650

Silicon Carbide Brick

Al2O3 ≥/%: 60-65
Bulk Density: 2.55-2.65g/cm³
Sample: testing of sample is available
Cold crushing strength: 85-90MPa

Sillimanite Brick

Al2O3: ≥60-65%;
SiO2: ≥32-37%;
Bulk Density: 2.40-2.55g/cm³;
Cold Crushing Strength: 45-60MPa;

MgO+CaO% (≥)：92-94;
CaO% (≥)：18-48;
Apparent Porosity(%)：15.0;
Cold Crushing Strength (MPa)：60;

Acid Proof Brick

Acid Resistance ≥/%: 99.8
Water Absorption ≤/%: 2
Bulk Density/ (g/cm³): 2.31-2.4
Bending strength/ (MPa): ≥58.80

Fire Clay Brick

Al2O3(%)≥: 40-77
Fe2O3(%)≤: 0.5-1.0
Bulk Density (g/cm³)≤: 0.55-1.35
Cold Crushing Strength (MPa)≥: 0.9-3.5

Insulation Bricks

High Alumina Insulation Brick

Al2O3≥: 48%
Fe2O3≤: 2.0%
Bulk Density (g/cm³): 0.5-1.2
Cold Crushing Strength(MPa)≥: 1.2-4.5

Silica Insulation Brick

SiO2% (≥): 91
Bulk Density (g/cm³): 1.0-1.2
Refractoriness Under Load (℃)≥: 1400-1520
Cold Crushing Strength (MPa)≥: 2.0-5.0

Mullite Insulation Brick

Al2O3(%)≥: 40-77
Fe2O3(%)≤: 0.5-1.0
Bulk Density (g/cm³)≤: 0.55-1.35
Cold Crushing Strength (MPa)≥: 0.9-3.5

Clay Insulation Brick

Bulk Density (g/cm³)≤: 0.5-1.5
Thermal Conductivity (W/m·k)≤: 0.23-0.65
Cold Crushing Strength (MPa)≥: 0.8-6
Permanent Linear Change/%: -2-1

Bubble Alumina Brick

Al2O3≥/%: 90-99
ω (SiO2) ≤/%: 0.3
Bulk Density (g/cm³): 1.3-1.9
Cold Crushing Strength ≥/MPa: 6-18

Monolithic Refractories

Refractory Castables

Al2O3%: 40-95
Bulk Density: (g/cm³): 1.8-2.5
Compressive Strength: (MPa): 20-150
Max Service Temperature: (℃): 1300-1800

Al2O3: 30-90
Bulk Density (g/cm³): 1.9-3.15
Compressive Strength (MPa): 20-100
Max Working Temperature/℃: 1400-1800

Refractory Mortar

Al2O3%: 40-78
Fe2O3%: 0.7-1.2
Classification Temperature/℃: 1300-1600
Refractoriness Underload/℃: 1320-1600

Refractory Cement

Al2O3% (≥): 50-81
Fineness(d50/μm): 5-13
Flexural Strength(72h)/Mpa: 6-12.5
Compressive Strength (72hrs)/MPa: 40-82

High Alumina Cement

Al2O3%: 50-81
Fineness(d50/μm): 5-13
Flexural Strength/Mpa(24h): 5.0-10.5
Compressive Strength/Mpa(24h): 30-72

Calcium Aluminate Cement

Al2O3(%): 50-81
CaO(%): 17.5-30.5
Fineness(d50/μm): 5-13
Compressive Strength (72hrs) (MPa):40-82

Low Cement Castable

Al2O3≥/%: 45-92
SiO2≥/%: 5-50
Bulk Density (g/cm³): 2.3-3
Cold Crushing Strength/Mpa: 72-85

Corundum Refractory Castable

Al2O3 ≥/%: 80-95
Bulk Density≥/(g/cm³): 2.7-3.2
Flexural Strength ≥/MPa: 9-11
Compressive Strength ≥/MPa: 60

Mullite Refractory Castable

Al2O3≥/%: 55-70
Bulk Density≥/(g/cm³): 2.3-2.6
Flexural Strength ≥/MPa: 7-9
Max Service Temperature (℃): 1300-1500

Lightweight Insulation Castable

Bulk Density(g/cm³): 0.5-1.8
Max. Service Temperature/℃: 1150-1350
Cold Crushing Strength(110℃*24h)≥: 1.5-20MPa
Thermal Conductivity (W/m·k)350℃: 0.15-0.65

High Alumina Refractory Castable

Al2O3≥/%: 50-80
Bulk Density ≥/ (g/cm³): 2.15-2.65
Cold Modulus of Rupture ≥/MPa: 4-7
Cold Crushing Strength ≥/Mpa: 25-40

Corundum Mullite Castable

Maximum Service Temperature ℃: 1550
Bulk Density(g/cm³)≥ : 2.7
1100℃ Cold Crushing Strength(Mpa) ≥ : 100
Linear Dimensional Change % ≤ : -0.3

Acid Resistant Castable

SiO2% (≥): 45-52
Bulk Density (g/cm³): 1.6-2
Acid Resistance% (≥): 95
Cold Crushing Strength (MPa): 5-10

Wear Resistant Castable

Al2O3≥/%: 70-85
Bulk Density ≥/ (g/cm³): 2.8-3.1
High strength and wear resistance
High density, low porosity

Silicon Carbide Castable

SiC+C≥/%: 58-83
Good resistance to erosion
Abrasiveness resistance
For cement kiln, EAF and steel ladel

Ultra Low Cement Castable

Al2O3 ≥/%: 45-95
Cao≥/%: 1.15
Bulk Density (g/cm3) ≥2.35-3.2
Refractoriness ≥1710-1790℃

Steel Fiber Castable

Al2O3 ≥/%: 70-80
Better thermal shock resistance
Used in building material industry
Sample: testing of sample is available

Plastic Refractory

Plasticity Index%：12-35
Al2O3% (≥)：35-80
Bulk Density (g/cm³)：2.15-2.65
Compressive Strength (Mpa)：6.0-8.0

Al2O3% (≥): 32-70
Fe2O3% (≥): 1.1-4.5
Type：Dense Gunning Material
Shelf Life (months)：9

Acid Resistant Mortar

Strong Acid Resistance
Good Adhesion
High Sealing Performance
Good Heat Resistance

Ceramic Fiber

Ceramic Fiber Blanket

Al2O3≥/%: 35-52
Bulk Density (g/cm³): 64-128
Classification Temperature (℃): 1260-1430
Shot Content ≤/%: 12-15

Ceramic Fiber Board

Modules of Rupture ≥/MPa: 0.3
Bulk Density (g/cm³): 250-360
Classification Temperature (℃): 1260-1430
Loss of Ignition ≤/%: 6

Ceramic Fiber Cloth

Color: White
Organic Content ≤/%: 15
Bulk Density (kg/m³): 500
Continuous Temperature Use Limit/℃: 650-1000

Ceramic Fiber Paper

Bulk Density (g/cm³): 200-240
Classification Temperature (℃): 1260-1350
Tensile Strength/MPa: 0.4-0.7
Thickness (mm): 0.5-6.4

Ceramic Fiber Cotton

Al2O3≥/%: 35-52
SiO2≥/%: 47-55
Classification Temperature (℃):1260-143
Shot Content ≤/%:12-15

Ceramic Fiber Rope

Bulk Density (g/cm³): 380-500
Continuous Temperature Use Limit/℃: 650-1000
Organic Content ≤/%: 15
Reinforcement: Glass Fiber/Stainless Steel

Ceramic Fiber Tape

Color: White
Organic Content ≤/%: 15
Bulk Density (kg/m³): 500
Continuous Temperature Use Limit/℃: 650-1000

Ceramic Fiber Module

Al2O3% (≥): 35-52
Bulk Density (g/cm³): 160-220
Classification Temperature (℃): 1260-1430
Permanent Linear Change ≤/%: 2.5-3.0

Calcium Silicate Board

Thickness: 6-18mm
Bulk Density (kg/m³): 230±10%
Modules of Rupture ≥/MPa: 0.45-0.55
Compressive Strength ≥/MPa: 0.75 -0.95

Kiln Furniture/Shelves

Kiln Furniture/Shelves

Silicon Carbide Kiln Furniture
Cordierite Mullite Kiln Shelves
For Ceramic and Glass Industries
Factory Supply, Lower Price

Honeycomb Ceramic Regenerator

Al2O3≥/%: 90-99
ω (SiO2) ≤/%: 0.3
Bulk Density (g/cm³): 1.3-1.9
Cold Crushing Strength ≥/MPa: 6-18