Silicon Carbide Batts RBSIC / SiSiC for Kiln Shelves
- Type: Beam, Batt, Plate, Roller, Tube, Sagger, Nozzle
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
Silicon Carbide Beam RBSIC / SiSiC for Kiln Shelves
- Type: Beam, Batt, Plate, Roller, Tube, Sagger, Nozzle
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
Silicon Carbide Rollers RBSIC / SiSiC for Kiln Furniture
- Type: Beam, Batt, Plate, Roller, Tube, Sagger, Nozzle
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
Silicon Carbide Saggers RBSIC / SiSiC for Kiln Furniture
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
- Good thermal conductivity: >24W/mK
Silicon Carbide Plates RBSIC / SiSiC for Kiln Shelves
- Type: Beam, Batt, Plate, Roller, Tube, Sagger, Nozzle
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
Silicon Carbide Burner Nozzles RBSIC / SiSiC for Kiln Furniture
- Type: Beam, Batt, Plate, Roller, Tube, Sagger, Nozzle
- Recrystallized SiC: >99.5%
- Bulk density: 2.45-2.65g/cm3
- Bending strength: >100MPa
- Compression strength: >600MPa
- Max working Temperature: 1650℃
Cordierite Mullite Kiln Shelves
- Bulk Density/g·cm3: ≥1.85
- Apparent Porosity/%: 26士4
- Room Temperature Flexural Strength/MPa: ≥10
- High Temperature Flexural Strength (1250℃*0.5h)/MPa: ≥9
- Thermal Expansion Coefficient (20℃~1000℃)/10-6 ℃-1: ≤2.8
- Processing Service: Bending, Welding, Punching, Decoiling, Cutting, Moulding