High alumina cement (formerly known as bauxite cement) is a hydraulic cementitious material with aluminate as the main mineral component, which is prepared by bauxite and lime in a certain proportion, calcined and ground, also known as aluminate cement.
| Item/Grade | CA50 | CA70 | CA80 | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
| Chemical Composition | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
| ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
| ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| Fineness | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
| -45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
| Setting Time | Initial Setting Time (min) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
| Final Setting Time (min) | ≤360 | ≤360 | ≤360 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
| Strength (ISO) | Flexural Strength/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
| 72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
| Compressive Strength/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
| 72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
| 325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
| Specific Surface Areas ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / | ||
In addition, we also supply: CA40/41 Cement
1.Large Heat of Hydration
2.Strong Resistance to Sulfate Erosion
3.Good High Temperature Resistance
4.Early Strength Characteristics
1. Flues, kilns, heat treatment furnaces and other building parts 2. Blast furnaces, converters, electric furnaces, etc., can be used as lining materials 3. Lining and protection of oil refining equipment, chemical furnaces, reactors 4. Maintenance and protection of high-temperature equipment such as electric furnaces, boilers, chimneys 5. Lining and protective layer of glass melting furnaces 6. Maintenance and protection of ladles, steel ladles, steelmaking furnaces, and continuous casting equipment.
The entire delivery process is tracked, and Kerui’s expert team solves specific project needs with the utmost professionalism. If the customer’s project requires it, Kerui’s expert team will go to the customer’s country to provide face-to-face technical support.
Besides mainland China, Kerui Refractory has exported products to more than 50 countries and regions across 5 continents across the world, including Asia, Europe, America, Africa and Oceania. We have received recognition and high praise from customers all over the world, and are constantly receiving customers’ return orders and referrals.