Alumina Silica Fire Brick is a kind of alumina silica refractory materials, which is widely applied for various parts of industrial furnaces such as coke ovens, hot blast stoves, glass kiln and steelmaking electric furnaces. Alumina Silica Refractory Brick includes many types as belows:
- Al2O3: 48-80%;
- Refractoriness Under Load: 1420-1530℃;
- Cold crushing strength: 40-70MPa;
- Sample: available;
- SiO2%: ≥94
- Fe2O3/%: ≤1.4
- Refractoriness Under Load (℃): ≥1650
- Sample: testing of sample is available
- Al2O3/%: 95-98
- SiO2/%: 0.15-0.5
- Cold crushing strength: 80-100MPa
- ISO9001/ISO14001/ISO45001/ISO50001
- Al2O3≥/%: 25-42
- Fe2O3)≤/%: 2.0
- Sample: testing of sample is available
- Cold Crushing Strength (MPa): 15-45
- ZrO2%: ≥ 16
- Fe2O3%: ≤ 0.5
- Bulk Density (g/cm³): ≥ 2.70
- Cold Crushing Strength/MPa: ≥ 70
- Apparent porosity %: ≤20
- Refractoriness under load°C: ≥1650℃
- Al2O3: ≥45%
- Bulk density g/cm3: ≥3.2
- Al2O3% (≥): 62-70
- Fe2O3)/%(≤): 1.5-1.8
- Refractoriness Under Load (℃)(≥): 1760-1780
- Cold Crushing Strength (MPa)(≥): 25
- Al2O3: ≥55%;
- Fe2O3: ≤1-1.5%;
- Bulk Density: 2.30-2.70g/cm³;
- Refractoriness Under Load: ≥1450-1700ºC;
- Al2O3(%)≥: 42-72
- Fe2O3(%)≤: 0.5-1.0
- Bulk Density (g/cm³)≤: 0.6-1.1
- Cold Crushing Strength (MPa)≥: 1.5-3.5
Alumina silica fire brick is based on AL2O3—SiO2 basic theory, including several below:
Silica brick, means refractory brick with over 93% SiO2 content, is a kind of acid refractory brick, mainly used for coke oven, glass kiln, ceramic kiln, carbon calcinations furnace, but not suitable for heating equipment with temperature fluctuation under 600 ℃.
Fire Clay Brick is mainly made of mullite, glass phase, cristobalite and quartz. Fireclay brick is always used in Blast Furnace, hot blast heater, heating furnace, power boiler, lime kiln, rotary kiln, ceramic kiln and calcining kiln.
High alumina brick is made of corundum, mullite and glass phase, which is subjected by AL2O3/ SiO2 proportions. High alumina brick is mainly used in steel manufacture, non-ferrous metals industry and other industries.
Corundum brick has over 90% AL2O3 content and with corundum as the main phase. Corundum brick can be classified into sintered corundum brick and fused cast corundum brick.
In addition, we also have a large number of AZS bricks, zirconium corundum bricks, andalusite bricks, mullite refractory bricks, mullite insulation bricks, etc. in stock, welcome to your inquiry!