Bata Api Alumina Silika

Alumina Silica Fire Brick is a kind of alumina silica refractory materials, which is widely applied for various parts of industrial furnaces such as coke ovens, hot blast stoves, glass kiln and steelmaking electric furnaces. Alumina Silica Refractory Brick includes many types as belows:

  • Al2O3: 48-80%;
  • Refraktilitas Di Bawah Beban: 1420-1530 ℃;
  • Kekuatan penghancuran dingin: 40-70MPa;
  • Sampel: tersedia;

  • SiO2%: ≥94
  • Fe2O3 / %: ≤1,4
  • Refraktilitas Di Bawah Beban (℃): ≥1650
  • Sampel: pengujian sampel tersedia

  • Al2O3 / %: 95-98
  • SiO2 / %: 0,15-0,5
  • Kekuatan penghancur dingin: 80-100MPa
  • ISO9001/ISO14001/ISO45001/ISO50001

  • Al2O3≥ / %: 25-42
  • Fe2O3) ≤ / %: 2.0
  • 0.2MPa Refraktori Di Bawah Beban T0.6 / ℃ (≥): 1250-1440
  • Kekuatan Penghancuran Dingin (MPa): 15-45

  • ZrO2%: ≥ 16
  • Fe2O3%: ≤ 0,5
  • Kepadatan Massal (g/cm³): ≥ 2,70
  • Kekuatan Penghancuran Dingin / MPa: ≥ 70

  • Porositas yang tampak %: ≤20
  • Refraktilitas di bawah beban ° C: ≥1650 ℃
  • Al2O3: ≥45%
  • Kepadatan massal g/cm3: ≥3,2

  • Al2O3% (≥): 62-70
  • Fe2O3) / % (≤): 1.5-1.8
  • Refraktilitas Di Bawah Beban (℃) (≥): 1760-1780
  • Kekuatan Penghancuran Dingin (MPa) (≥): 25

  • Al2O3: ≥55%;
  • Fe2O3: ≤1-1.5%;
  • Bulk Density: 2.30-2.70g/cm³;
  • Refractoriness Under Load: ≥1450-1700ºC;

  • Al2O3 (%) ≥: 42-72
  • Fe2O3 (%) ≤: 0.5-1.0
  • Kepadatan Massal (g/cm³) ≤: 0.6-1.1
  • Kekuatan Penghancuran Dingin (MPa) ≥: 1.5-3.5

    Hubungi Kami

    Silakan kirim pertanyaan untuk mendapatkan info detail dan harga terbaik:

    * Nama:

    * Email:

    Telepon/Whatsapp:

    Negara:

    *Pesan:

    DAPATKAN HARGA
    X DAPATKAN HARGA

      Hubungi Kami

      Silakan kirim pertanyaan untuk mendapatkan info detail dan harga terbaik:

      * Nama:

      * Email:

      Telepon/Whatsapp:

      Negara:

      *Pesan: