Monolithic Refractory

Refractory Castables

Al2O3%: 40-95
Bulk Density: (g/cm³): 1.8-2.5
Compressive Strength: (MPa): 20-150
Max Service Temperature: (℃): 1300-1800

Ramming Mass

Al2O3: 30-90
Bulk Density (g/cm³): 1.9-3.15
Compressive Strength (MPa): 20-100
Max Working Temperature/℃: 1400-1800

Refractory Mortar

Al2O3%: 40-78
Fe2O3%: 0.7-1.2
Classification Temperature/℃: 1300-1600
Refractoriness Underload/℃: 1320-1600

Refractory Cement

Al2O3% (≥): 50-81
Fineness(d50/μm): 5-13
Flexural Strength(72h)/Mpa: 6-12.5
Compressive Strength (72hrs)/MPa: 40-82

High Alumina Cement

Al2O3%: 50-81
Fineness(d50/μm): 5-13
Flexural Strength/Mpa(24h): 5.0-10.5
Compressive Strength/Mpa(24h): 30-72

Calcium Aluminate Cement

Al2O3(%): 50-81
CaO(%): 17.5-30.5
Fineness(d50/μm): 5-13
Compressive Strength (72hrs) (MPa):40-82

Low Cement Castable

Al2O3≥/%: 45-92
SiO2≥/%: 5-50
Bulk Density (g/cm³): 2.3-3
Cold Crushing Strength/Mpa: 72-85

Corundum Refractory Castable

Al2O3 ≥/%: 80-95
Bulk Density≥/(g/cm³): 2.7-3.2
Flexural Strength ≥/MPa: 9-11
Compressive Strength ≥/MPa: 60

Mullite Refractory Castable

Al2O3≥/%: 55-70
Bulk Density≥/(g/cm³): 2.3-2.6
Flexural Strength ≥/MPa: 7-9
Max Service Temperature (℃): 1300-1500

Lightweight Insulation Castable

Bulk Density(g/cm³): 0.5-1.8
Max. Service Temperature/℃: 1150-1350
Cold Crushing Strength(110℃*24h)≥: 1.5-20MPa
Thermal Conductivity (W/m·k)350℃: 0.15-0.65

High Alumina Refractory Castable

Al2O3≥/%: 50-80
Bulk Density ≥/ (g/cm³): 2.15-2.65
Cold Modulus of Rupture ≥/MPa: 4-7
Cold Crushing Strength ≥/Mpa: 25-40