Sintered Magnesite

Sintered magnesia is divided into dead-burned magnesia, medium-grade magnesia and high-purity magnesia according to the preparation process and the mass fraction of magnesium oxide.

  • w(MgO)≥/%: 90.0-97.7
  • w(SiO2)≤/%: 0.3-4.8
  • Volume density/g·cm3(≥): 3.18-3.40

Description of Sintered Magnesite

Sintered magnesia is generally made by directly calcining magnesite in a vertical kiln or a rotary kiln. The grade of sintered magnesia is calibrated by the mass fraction of MgO, and the highest grade can generally reach w(MgO)=98%. The main impurities in the raw materials are SiO2 and CaO, and the mass fraction of Fe2O3 is not high.

Kerui Sintered Magnesite Technical Data Sheet

Type w(MgO)/% w(SiO2)/% w(CaO)/% CaO/SiO2 molar ratio Volume density/g·cm3
MS98A ≥97.7 ≤0.3 / ≥3 ≥3.40
MS98B ≥97.7 ≤0.4 / ≥2 ≥3.35
MS98C ≥97.5 ≤0.4 / ≥2 ≥3.30
MS97A ≥97.0 ≤0.5 / ≥2 ≥3.40
MS97B ≥97.0 ≤0.6 / ≥2 ≥3.35
MS97C ≥97.0 ≤0.8 / / ≥3.30
MS96A ≥96.0 ≤1.0 / / ≥3.30
MS96B ≥96.0 ≤1.5 / / ≥3.25
MS95A ≥95.0 ≤2.0 ≤1.6 / ≥3.25
MS95B ≥95.0 ≤2.2 ≤1.6 / ≥3.20
MS93A ≥93.0 ≤3.0 ≤1.6 / ≥3.20
MS93B ≥93.0 ≤3.5 ≤1.6 / ≥3.18
NS90A ≥90.0 ≤4.0 ≤1.6 / ≥3.20
NS90B ≥90.0 ≤4.8 ≤2.0 / ≥3.18

Types of Sintered Magnesite

1. Heavy burned magnesia sand

Heavy burned magnesite sand is sintered at 1600 – 1900℃ from magnesite, seawater/magnesium hydroxide. China uses >46% MgO magnesite lump with solid fuel in vertical kiln, yielding 89% – 98% MgO dead burn magnesite sand.

IL 二酸化ケイ素 CAO MgO Al2O3 Fe2O3 Volume density/g·cm-3
0.27 3.87 1.86 92.48 0.62 0.90 3.16

2. Mid-grade magnesium sand

Using MgO mass fraction greater than 46.5% of magnesite, lightly burned by the reflection furnace, and then finely ground, mixed with water, ball pressed, mixed with solid fuel blocks into the vertical kiln calcined production of magnesium sand.MgO mass fraction of about 95%, also known as mid-range magnesium sand.

IL 二酸化ケイ素 CAO MgO Al2O3 Fe2O3 Bulk density/g-cm-3
0.50 1.95 1.58 94.63 0.34 1.00 3.17

3. High-purity magnesium sand

The use of MgO mass fraction greater than 47% of magnesite, lightly burned to obtain a good high purity of lightly burned magnesium powder as raw material, by fine grinding, dry ball pressing, into the ultra-high temperature oil vertical kiln calcination production of magnesium sand MgO mass fraction of 96.5% to 98%, known as high purity magnesium sand.

IL 二酸化ケイ素 CAO MgO Al2O3 Fe2O3 Volume density/g·cm-3
0.30 0.70 1.35 96.90 0.25 0.80 3.20

4. Seawater magnesium sand

China’s abundant magnesite reserves have long led metallurgical firms to mainly produce low-grade magnesium sand from magnesite. Two-step calcination can make high-purity magnesium sand with ~97% purity, but ≥99% ultra-high-purity sand via heavy firing remains tough. Producing ≥98%/≥99% sand from seawater/brine is easier, with MgO up to 99.5%.

IL 二酸化ケイ素 CAO MgO Al2O3 Fe2O3 Volume density/g·cm-3
0.25 0.23 0.53 98.85 0.03 0.11 3.20

Applications of Sintered Magnesite

In steel industry, sintered magnesia makes refractory bricks/linings to resist high temps & corrosion. In non-ferrous smelting, it protects equipment. For coatings/castables, it boosts heat resistance & strength. Also used in ceramics/abrasives for hardness/stability.

ケルイ耐火物研究所

ケルイには専門の品質検査室があります。高温再加熱/荷重軟化クリープ試験炉;耐火物圧縮/曲げ強度試験台;耐火物組成試験及び検査プラットフォーム;耐火物物理/化学特性実験室。