The main raw material of magnesia bricks is burned magnesia or electric fused magnesia,High pressure forming,high-temperature 1600-1700°C sintering,MgO content is above 91%. KERUI is a professional manufacturer of magnesia bricks, welcome to inquire!
| アイテム/グレード | M-98 | M-97A | M-97B | M-95A | M-95B | M-91 | M-89 | |
|---|---|---|---|---|---|---|---|---|
| ω (MgO)/% | μ0 ≥ | 97.5 | 97.0 | 96.5 | 95.0 | 94.5 | 91.0 | 89.0 |
| σ | 1.0 | 1.5 | ||||||
| ω (SiO2)/% | μ0 ≤ | 1.00 | 1.20 | 1.50 | 2.00 | 2.50 | / | / |
| σ | 0.30 | |||||||
| ω (CaO)/% | μ0 ≤ | / | / | / | 2.00 | 2.00 | 3.00 | 3.00 |
| σ | 0.30 | |||||||
| 見掛け気孔率/% | μ0 ≤ | 16 | 16 | 18 | 16 | 18 | 18 | 20 |
| σ | 1.5 | |||||||
| かさ密度 (g/cm³) | μ0 ≥ | 3.00 | 3.00 | 2.95 | 2.90 | 2.85 | ||
| σ | 0.30 | |||||||
| 冷間圧壊強さ/MPa | μ0 ≥ | 60 | 60 | 60 | 60 | 50 | ||
| X分 | 50 | 50 | 50 | 50 | 45 | |||
| σ | 10 | |||||||
| 0.2MPa耐屈折下荷重/℃（0.2MPaの場合 | μ0 ≥ | 1700 | 1700 | 1650 | 1560 | 1500 | ||
| σ | 15 | |||||||
| パーマネント・リニア・チェンジ/% | X分~Xマックス | 1650℃*2h -0.2-0 | 1650℃*2h -0.3-0 | 1600℃*2h -0.5-0 | 1600℃*2h -0.6-0 | |||
1.Refractory Performance
2.Excellent Slag Resistance
3.Good Thermal Conductivity
4.Long Life and Durability
5.Rapid Cooling and Thermal Expansion Adaptability
Magnesia bricks are mainly used in steel-making furnaces, cement kilns, glass furnaces, etc., due to their high refractoriness and good slag resistance.
私達は専門の技術的なチームおよび生産設備が付いている私達の自身の工場を持っています。 全自動バッチシステム 400-1000トンの成形プレス20セット； 2 * 168mの高温トンネルキルン； 20000㎡の倉庫。 製品の品質を確保し、生産効率を向上させ、顧客に最も満足のいく製品とサービスを提供する。
納品プロセス全体が追跡され、Keruiの専門家チームが最高のプロフェッショナリズムで特定のプロジェクトニーズを解決します。お客様のプロジェクトが必要とする場合、Keruiの専門家チームはお客様の国へ出向き、対面での技術サポートを提供します。