Basic Refractory Bricks are a type of refractory material. They mainly consist of alkaline oxides like magnesia and calcium oxide. They have good resistance to high temperatures and basic slag corrosion. Widely used in steel – making furnaces, glass kilns, etc., they play a crucial role in high – temperature industrial applications. The following are several common KERUI Basic Refractory Bricks. If you have any needs, please contact us to get the best quotation!
CALIENTE
- MgO% (≥): 89-97.5
- Densidad aparente (g/cm³): 2.85-3.0
- Refractariedad bajo carga (℃): 1500-1700
- Resistencia al aplastamiento en frío (MPa): 45-60
CALIENTE
- MgO Composición química :≥95 ％;
- Porosidad aparente :≤18 ％;
- Resistencia al aplastamiento en frío :≥55 Mpa;
- Estabilidad térmica 950℃ Ciclos de viento:≥15;
CALIENTE
- MgO%: 69-85
- C%: 5-18
- Densidad aparente (g/cm³): 2.79-3.05
- Resistencia al aplastamiento en frío (MPa): 30-50
CALIENTE
- MgO%(≥): 45-65
- Cr2O3%(≥): 8-16
- Porosidad aparente/%(≤): 19-21
- Resistencia al aplastamiento en frío (MPa): 20-35
CALIENTE
- MgO% ≥：70/75/80 ZrO2 %≥：8/10/13;
- Porosidad aparente%≤：19;
- Densidad aparente (g/cm3)≥：2,95;
- Refractariedad bajo carga:≥1600 °C
CALIENTE
- MgO/%(≥): 80;
- Al2O3/%(≥): 10
- Densidad aparente (g/cm³)(≥): 2.90
- Resistencia al aplastamiento en frío(≥): 50MPa