High alumina cement (formerly known as bauxite cement) is a hydraulic cementitious material with aluminate as the main mineral component, which is prepared by bauxite and lime in a certain proportion, calcined and ground, also known as aluminate cement.
| Στοιχείο/βαθμός | CA50 | CA70 | CA80 | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
| Χημική σύνθεση | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
| ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
| ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| Λεπτότητα | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
| -45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
| Χρόνος ρύθμισης | Χρόνος αρχικής ρύθμισης (λεπτά) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
| Τελικός χρόνος σκλήρυνσης (λεπτά) | ≤360 | ≤360 | ≤360 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
| Αντοχή (ISO) | Αντοχή σε κάμψη/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
| 72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
| Αντοχή σε θλίψη/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
| 72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
| 325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
| Ειδικές επιφάνειες ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / | ||
In addition, we also supply: CA40/41 Τσιμέντο
1.Large Heat of Hydration
2.Strong Resistance to Sulfate Erosion
3.Good High Temperature Resistance
4.Early Strength Characteristics
1. Flues, kilns, heat treatment furnaces and other building parts 2. Blast furnaces, converters, electric furnaces, etc., can be used as lining materials 3. Lining and protection of oil refining equipment, chemical furnaces, reactors 4. Maintenance and protection of high-temperature equipment such as electric furnaces, boilers, chimneys 5. Lining and protective layer of glass melting furnaces 6. Maintenance and protection of ladles, steel ladles, steelmaking furnaces, and continuous casting equipment.
Ολόκληρη η διαδικασία παράδοσης παρακολουθείται και η ομάδα εμπειρογνωμόνων της Kerui επιλύει τις συγκεκριμένες ανάγκες του έργου με απόλυτο επαγγελματισμό. Εάν το έργο του πελάτη το απαιτεί, η ομάδα εμπειρογνωμόνων της Kerui θα μεταβεί στη χώρα του πελάτη για να παράσχει προσωπική τεχνική υποστήριξη.
Εκτός από την ηπειρωτική Κίνα, η Kerui Refractory έχει εξάγει προϊόντα σε περισσότερες από 50 χώρες και περιοχές σε 5 ηπείρους σε όλο τον κόσμο, συμπεριλαμβανομένης της Ασίας, της Ευρώπης, της Αμερικής, της Αφρικής και της Ωκεανίας. Έχουμε λάβει αναγνώριση και υψηλούς επαίνους από τους πελάτες σε όλο τον κόσμο και λαμβάνουμε συνεχώς τις παραγγελίες επιστροφής και τις παραπομπές των πελατών.