The main raw material of magnesia bricks is burned magnesia or electric fused magnesia,High pressure forming,high-temperature 1600-1700°C sintering,MgO content is above 91%. KERUI is a professional manufacturer of magnesia bricks, welcome to inquire!
| الصنف/الرتبة | M-98 | M-97A | M-97B | M-95A | M-95B | M-91 | M-89 | |
|---|---|---|---|---|---|---|---|---|
| ω (MgO)/% | μ0 ≥ | 97.5 | 97.0 | 96.5 | 95.0 | 94.5 | 91.0 | 89.0 |
| σ | 1.0 | 1.5 | ||||||
| ω (SiO2)/% | μ0 ≤ | 1.00 | 1.20 | 1.50 | 2.00 | 2.50 | / | / |
| σ | 0.30 | |||||||
| ω (CaO) / % | μ0 ≤ | / | / | / | 2.00 | 2.00 | 3.00 | 3.00 |
| σ | 0.30 | |||||||
| المسامية الواضحة/% | μ0 ≤ | 16 | 16 | 18 | 16 | 18 | 18 | 20 |
| σ | 1.5 | |||||||
| الكثافة السائبة (جم/سم مكعب) | μ0 ≥ | 3.00 | 3.00 | 2.95 | 2.90 | 2.85 | ||
| σ | 0.30 | |||||||
| قوة السحق على البارد/ميجا باسكال | μ0 ≥ | 60 | 60 | 60 | 60 | 50 | ||
| Xدقيقة | 50 | 50 | 50 | 50 | 45 | |||
| σ | 10 | |||||||
| 0.2 ميجا باسكال انكسار الحمل المنخفض/ ℃ | μ0 ≥ | 1700 | 1700 | 1650 | 1560 | 1500 | ||
| σ | 15 | |||||||
| تغيير خطي دائم/%/% | Xدقيقة~Xالحد الأقصى | 1650℃*2h -0.2-0 | 1650℃*2h -0.3-0 | 1600℃*2h -0.5-0 | 1600℃*2h -0.6-0 | |||
1.Refractory Performance 2.Excellent Slag Resistance 3.Good Thermal Conductivity 4.Long Life and Durability 5.Rapid Cooling and Thermal Expansion Adaptability
Magnesia bricks are mainly used in steel-making furnaces, cement kilns, glass furnaces, etc., due to their high refractoriness and good slag resistance.