High alumina brick is a kind of aluminum silicate refractory product with aluminum oxide (Al2O3) content higher than 80%. It is formed and calcined from bauxite or other raw materials with high alumina content. High thermal stability, refractoriness above 1770°C. It has good slag resistance and is used for the lining of masonry steelmaking electric furnaces, glass melting furnaces, and cement rotary furnaces.
| الصنف/الرتبة | LZ-80 | LZ-75 | LZ-70 | LZ-65 | LZ-55 | LZ-48 | LZ-75G | LZ-65G | LZ-55G | |
|---|---|---|---|---|---|---|---|---|---|---|
| ω (Al2O3)/% | μ0 ≥ | 80 | 75 | 70 | 65 | 55 | 48 | 75 | 65 | 55 |
| σ | 1.5 | |||||||||
| Apparent Porosity/% | μ0 ≤ | 21 (23) | 24 (26) | 24 (26) | 24 (26) | 22 (24) | 22 (24) | 19 | 19 | 19 |
| σ | 1.5 | |||||||||
| قوة السحق على البارد/ميجا باسكال | μ0 ≥ | 70 (60) | 60 (50) | 55 (45) | 50 (40) | 45 (40) | 40 (35) | 65 | 60 | 50 |
| Xmin | 60 (50) | 50 (40) | 45 (35) | 40 (30) | 35 (30) | 30 (35) | 55 | 50 | 40 | |
| σ | 15 | |||||||||
| 0.2MPa Refractoriness Underload/℃ | μ0 ≥ | 1530 | 1520 | 1510 | 1500 | 1450 | 1420 | 1520 | 1500 | 1470 |
| σ | 13 | |||||||||
| تغيير خطي دائم/%/% | Xmin Xmax | 1500℃*2h -0.4~0.2 | 1450℃*2h -0.4~0.1 | 1500℃*2h -0.2~0.1 | 1450℃*2h -0.2~0 | |||||
High refractoriness； Excellent thermal shock resistance； Excellent slag resistance； Excellent slag resistance； Low Thermal Conductivity；