Corundum bricks are refractory products with corundum as the main crystal phase, in which the Al2O3 content is greater than 90%. It has high compressive strength at room temperature (up to 340MPa). The load softening starting temperature is high (greater than 1700℃). There are two types of sintered corundum bricks and fused corundum bricks. It can be made of sintered corundum or fused corundum as raw materials, or bauxite clinker with a relatively high Al2O3/SiO2 and sintered corundum by sintering method. It can also be made of unburned corundum bricks using phosphoric acid or other binders.
| الصنف/الرتبة | GYZ-99A | GYZ-99B | GYZ-98 | GYZ-95 | |
|---|---|---|---|---|---|
| ω (Al2O3)/% | μ0 ≥ | 99.0 | 99.0 | 98.0 | 95.0 |
| ở | 0.30 | ||||
| ω (SiO2)/% | μ0 ≤ | 0.15 | 0.2 | 0.5 | / |
| ở | 0.08 | ||||
| ω (Fe2O3)/% | μ0 ≤ | 0.10 | 0.15 | 0.2 | 0.3 |
| ở | 0.03 | ||||
| Apparent Porosity/% | μ0 ≤ | 19 | 19 | 19 | 20 |
| ở | 1 | ||||
| الكثافة السائبة (جم/سم مكعب) | μ0 ≤ | 3.20 | 3.15 | 3.15 | 3.1 |
| ở | 0.05 | ||||
| قوة السحق على البارد/ميجا باسكال | μ0 ≥ | 80 | 80 | 80 | 100 |
| ở | 15 | ||||
| Permanent Linear Change (1600℃*3h)/% | Xmin Xmax | -0.2~+0.2 | -0.2~+0.2 | -0.2~+0.2 | -0.3~+0.3 |
| 0.2MPa 0.6% Refractoriness Underload/℃ | Xmin | 1700 | 1700 | 1700 | 1700 |
Main material of corundum mullite brick is imported plate corundum, high pure fused corundum, adopt advanced superfine powder adding technology, it is made by the mixing material, drying, molding and burned in high temperature shuttle kiln.
Fused corundum bricks are made by melting alumina in an electric arc furnace and casting it into a specified model of a specific shape. The desired product is obtained by annealing and holding, and then by processing with diamond abrasives.
Chrome corundum brick is also called high wear-resistant chrome corundum tapping brick. Using α-Al2O3 as raw material, appropriate amount of chromia powder and chrome corundum clinker fine powder are added, and then they are shaped and burned at high temperature. The main mineral composition is α-Al2O3-Cr2O3 solid solution. Minor minerals consist of a small amount of composite spinel (or no composite spinel), refractory bricks with 1% to 30% chromium oxide content.
High chromium bricks are made of chromium oxide and alumina as the main raw materials, or a small amount of zirconium oxide is introduced. After high temperature firing into. The content of chromium oxide is not less than 75%, and the content of chromium oxide and alumina is not less than 98% of the shaped refractory products. High chromium bricks have excellent resistance to leaching, high compressive strength at room temperature, excellent wear resistance, high temperature resistance, good thermal shock resistance, etc.
1.High Hardness 2.Corrosion Resistance 3.High Temperature Resistance 4.Dimensional Stability 5.Excellent Insulation Performance 6.Good Air Permeability
Used in iron-making blast furnaces and hot blast furnaces, steel-making furnace external refining furnaces, sliding water heaters, glass melting furnaces and petrochemical industrial furnaces.