镁碳砖是一种与碳粘结剂相结合的不燃碳复合耐火材料。它以高熔点碱性氧化物氧化镁（熔点 2800°C）和不易被熔渣侵蚀的高熔点碳素材料为原料，加入各种非氧化物添加剂，经高温烧成而成。作为一种复合耐火材料，镁碳砖有效利用了镁的强抗渣侵蚀性和碳的高导热性、低膨胀性，弥补了镁抗剥落性差的最大缺陷。
凯瑞镁碳砖技术数据表
| 项目/等级 | 表观孔隙率/% | 体积密度（克/立方厘米） | 冷压强度/兆帕 | 高温弯曲强度 (1400℃*0.5h)/MPa |
ω（氧化镁）/% | ω（C）/% | ||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| μ0 ≤ | σ | μ0 ≥ | σ | μ0 | σ | μ0 ≥ | σ | μ0 ≥ | σ | μ0 ≥ | σ | |
| MT-5A | 5.0 | 1.0 | 3.10 | 0.05 | 50.0 | 10.0 | / | / | 85.0 | 1.5 | 5.0 | 1.0 |
| MT-5B | 6.0 | 1.0 | 3.02 | 0.05 | 50.0 | 10.0 | / | / | 84.0 | 1.5 | 5.0 | 1.0 |
| MT-5C | 7.0 | 1.0 | 2.92 | 0.05 | 45.0 | 10.0 | / | / | 82.0 | 1.5 | 5.0 | 1.0 |
| MT-5D | 8.0 | 1.0 | 2.90 | 0.05 | 40.0 | 10.0 | / | / | 80.0 | 1.5 | 5.0 | 1.0 |
| MT-8A | 4.5 | 1.0 | 3.05 | 0.05 | 45.0 | 10.0 | / | / | 82.0 | 1.5 | 8.0 | 1.0 |
| MT-8B | 5.0 | 1.0 | 3.00 | 0.05 | 45.0 | 10.0 | / | / | 81.0 | 1.5 | 8.0 | 1.0 |
| MT-8C | 6.0 | 1.0 | 2.90 | 0.05 | 40.0 | 10.0 | / | / | 79.0 | 1.5 | 8.0 | 1.0 |
| MT-8D | 7.0 | 1.0 | 2.87 | 0.05 | 35.0 | 10.0 | / | / | 77.0 | 1.5 | 8.0 | 1.0 |
| MT-10A | 4.0 | 0.5 | 3.02 | 0.03 | 40.0 | 10.0 | 6.0 | 1.0 | 80.0 | 1.5 | 10.0 | 1.0 |
| MT-10B | 4.5 | 0.5 | 2.97 | 0.03 | 40.0 | 10.0 | / | / | 79.0 | 1.5 | 10.0 | 1.0 |
| MT-10C | 5.0 | 0.5 | 2.92 | 0.03 | 35.0 | 10.0 | / | / | 77.0 | 1.5 | 10.0 | 1.0 |
| MT-10D | 6.0 | 0.5 | 2.87 | 0.03 | 35.0 | 10.0 | / | / | 75.0 | 1.5 | 10.0 | 1.0 |
| MT-12A | 4.0 | 0.5 | 2.97 | 0.03 | 40.0 | 10.0 | 6.0 | 1.0 | 78.0 | 1.2 | 12.0 | 1.0 |
| MT-12B | 4.0 | 0.5 | 2.94 | 0.03 | 35.0 | 10.0 | / | / | 77.0 | 1.2 | 12.0 | 1.0 |
| MT-12C | 4.5 | 0.5 | 2.92 | 0.03 | 35.0 | 10.0 | / | / | 75.0 | 1.2 | 12.0 | 1.0 |
| MT-12D | 5.5 | 0.5 | 2.85 | 0.03 | 30.0 | 10.0 | / | / | 73.0 | 1.2 | 12.0 | 1.0 |
| MT-14A | 3.5 | 0.5 | 2.95 | 0.03 | 38.0 | 10.0 | 10.0 | 1.0 | 76.0 | 1.2 | 14.0 | 1.0 |
| MT-14B | 3.5 | 0.5 | 2.90 | 0.03 | 35.0 | 10.0 | / | / | 74.0 | 1.2 | 14.0 | 1.0 |
| MT-14C | 4.0 | 0.5 | 2.87 | 0.03 | 35.0 | 10.0 | / | / | 72.0 | 1.2 | 14.0 | 1.0 |
| MT-14D | 5.0 | 0.5 | 2.81 | 0.03 | 30.0 | 10.0 | / | / | 68.0 | 1.2 | 14.0 | 1.0 |
| MT-16A | 3.5 | 0.5 | 2.92 | 0.03 | 35.0 | 8.0 | 8.0 | 1.0 | 74.0 | 1.2 | 16.0 | 0.8 |
| MT-16B | 3.5 | 0.5 | 2.87 | 0.03 | 35.0 | 8.0 | / | / | 72.0 | 1.2 | 16.0 | 0.8 |
| MT-16C | 4.0 | 0.5 | 2.82 | 0.03 | 30.0 | 8.0 | / | / | 70.0 | 1.2 | 16.0 | 0.8 |
| MT-18A | 3.0 | 0.5 | 2.89 | 0.03 | 35.0 | 8.0 | 10.0 | 1.0 | 72.0 | 1.2 | 18.0 | 0.8 |
| MT-18B | 3.5 | 0.5 | 2.84 | 0.03 | 30.0 | 8.0 | / | / | 70.0 | 1.2 | 18.0 | 0.8 |
| MT-18C | 4.0 | 0.5 | 2.79 | 0.03 | 30.0 | 8.0 | / | / | 69.0 | 1.2 | 18.0 | 0.8 |
镁碳砖的优点
出色的耐高温性能
镁碳砖具有优异的高温性能，可在 1200 °C 以上长期使用。
耐腐蚀性
镁碳砖具有出色的耐腐蚀性，因此可用于酸碱等强腐蚀性环境。
良好的抗热震性
镁碳砖在高温下具有非常好的抗热震性能，可承受较大的温度梯度变化而不会开裂。
良好的导热性
镁碳砖具有良好的导热性，可以均匀分布和传递热量，有利于提高生产效率。
镁碳砖的应用
钢铁冶炼
镁碳砖广泛应用于钢铁冶炼行业的各种设备，如转炉、电弧炉、炼钢罐等。它们用作内衬材料，能够承受冶炼过程中产生的高温和熔融金属的腐蚀。
铝冶炼
镁碳砖还用于铝冶炼工业中的电解槽。电解槽是电解铝的主要设备，镁碳砖在电解槽中具有良好的耐火性和导电性。
钢包维修
在钢包维护和修理中，镁碳砖通常用于修复钢包底部和侧壁的耐火衬。这样可以延长钢包的使用寿命，确保钢水质量。
高温工业炉
镁碳砖适用于各种高温工业炉，如炼油炉、化工炉、玻璃熔化炉等。它们能够承受高温环境、化学侵蚀和热冲击应力。
机械制造业
镁碳砖可用于制造高性能电极、半导体工业炉料、高硼合金等。
高温反应堆
镁碳砖还可用于高温反应器，如氢氧化铝生产过程中的煅烧炉和氨合成过程中的转化炉。