Basic Refractory Bricks are a type of refractory material. They mainly consist of alkaline oxides like magnesia and calcium oxide. They have good resistance to high temperatures and basic slag corrosion. Widely used in steel – making furnaces, glass kilns, etc., they play a crucial role in high – temperature industrial applications. The following are several common KERUI Basic Refractory Bricks. If you have any needs, please contact us to get the best quotation!
SICAK
- MgO% (≥): 89-97.5
- Yığın Yoğunluğu (g/cm³): 2.85-3.0
- Yük Altında Refrakterlik (℃): 1500-1700
- Soğuk Kırılma Dayanımı (MPa): 45-60
SICAK
- MgO Kimyasal bileşim: ≥95 ％;
- Görünür Gözeneklilik: ≤18 ％;
- Soğuk Kırma Dayanımı: ≥55 Mpa;
- Termal Kararlılık 950 ℃ Rüzgar döngüleri: ≥15;
SICAK
- MgO%: 69-85
- C%: 5-18
- Yığın Yoğunluğu (g/cm³): 2.79-3.05
- Soğuk Kırılma Dayanımı (MPa): 30-50
SICAK
- MgO%(≥): 45-65
- Cr2O3%(≥): 8-16
- Görünür Gözeneklilik/%(≤): 19-21
- Soğuk Kırılma Dayanımı (MPa): 20-35
SICAK
- MgO% ≥：70/75/80 ZrO2 %≥：8/10/13;
- Görünür Gözeneklilik%≤：19;
- Yığın Yoğunluğu (g/cm3)≥：2,95;
- Yük Altında Refrakterlik: ≥1600 °C
SICAK
- MgO/%(≥): 80;
- Al2O3/%(≥): 10
- Yığın Yoğunluğu (g/cm³)(≥): 2.90
- Soğuk Kırılma Dayanımı (≥): 50MPa