Углеродистый магнезиальный кирпич

• MgO%: 69-85
• C%: 5-18
• Насыпная плотность (г/см³): 2.79-3.05
• Прочность на холодное раздавливание (МПа): 30-50
• Стандартный размер: 230*114*65 мм
• Сертификация: ISO9001/ISO14001/ISO45001/ISO50001
• Образец: тестирование образца доступно

Описание углеродистого магнезиального кирпича

Magnesia carbon brick is a non-burning carbon composite refractory material combined with carbon binder. Using high melting point basic oxide magnesium oxide (melting point 2800°C) and high melting point carbon material which is difficult to be infiltrated by slag as raw materials, various non-oxide additives are added. As a composite refractory material, magnesia carbon brick effectively utilizes the strong slag erosion resistance of magnesia and the high thermal conductivity and low expansion of carbon to compensate for the biggest shortcoming of magnesia’s poor spalling resistance.

Технические характеристики углеродистого кирпича Kerui Magnesia

Артикул/сорт	Кажущаяся пористость/%		Насыпная плотность (г/см³)		Прочность на холодное раздавливание/МПа		Прочность при высокотемпературном изгибе (1400℃*0.5h)/MPa		ω (MgO)/%		ω (C)/%
	μ0 ≤	σ	μ0 ≥	σ	μ0	σ	μ0 ≥	σ	μ0 ≥	σ	μ0 ≥	σ
MT-5A	5.0	1.0	3.10	0.05	50.0	10.0	/	/	85.0	1.5	5.0	1.0
MT-5B	6.0	1.0	3.02	0.05	50.0	10.0	/	/	84.0	1.5	5.0	1.0
MT-5C	7.0	1.0	2.92	0.05	45.0	10.0	/	/	82.0	1.5	5.0	1.0
MT-5D	8.0	1.0	2.90	0.05	40.0	10.0	/	/	80.0	1.5	5.0	1.0
MT-8A	4.5	1.0	3.05	0.05	45.0	10.0	/	/	82.0	1.5	8.0	1.0
MT-8B	5.0	1.0	3.00	0.05	45.0	10.0	/	/	81.0	1.5	8.0	1.0
MT-8C	6.0	1.0	2.90	0.05	40.0	10.0	/	/	79.0	1.5	8.0	1.0
MT-8D	7.0	1.0	2.87	0.05	35.0	10.0	/	/	77.0	1.5	8.0	1.0
MT-10A	4.0	0.5	3.02	0.03	40.0	10.0	6.0	1.0	80.0	1.5	10.0	1.0
MT-10B	4.5	0.5	2.97	0.03	40.0	10.0	/	/	79.0	1.5	10.0	1.0
MT-10C	5.0	0.5	2.92	0.03	35.0	10.0	/	/	77.0	1.5	10.0	1.0
MT-10D	6.0	0.5	2.87	0.03	35.0	10.0	/	/	75.0	1.5	10.0	1.0
MT-12A	4.0	0.5	2.97	0.03	40.0	10.0	6.0	1.0	78.0	1.2	12.0	1.0
MT-12B	4.0	0.5	2.94	0.03	35.0	10.0	/	/	77.0	1.2	12.0	1.0
MT-12C	4.5	0.5	2.92	0.03	35.0	10.0	/	/	75.0	1.2	12.0	1.0
MT-12D	5.5	0.5	2.85	0.03	30.0	10.0	/	/	73.0	1.2	12.0	1.0
MT-14A	3.5	0.5	2.95	0.03	38.0	10.0	10.0	1.0	76.0	1.2	14.0	1.0
MT-14B	3.5	0.5	2.90	0.03	35.0	10.0	/	/	74.0	1.2	14.0	1.0
MT-14C	4.0	0.5	2.87	0.03	35.0	10.0	/	/	72.0	1.2	14.0	1.0
MT-14D	5.0	0.5	2.81	0.03	30.0	10.0	/	/	68.0	1.2	14.0	1.0
MT-16A	3.5	0.5	2.92	0.03	35.0	8.0	8.0	1.0	74.0	1.2	16.0	0.8
MT-16B	3.5	0.5	2.87	0.03	35.0	8.0	/	/	72.0	1.2	16.0	0.8
MT-16C	4.0	0.5	2.82	0.03	30.0	8.0	/	/	70.0	1.2	16.0	0.8
MT-18A	3.0	0.5	2.89	0.03	35.0	8.0	10.0	1.0	72.0	1.2	18.0	0.8
MT-18B	3.5	0.5	2.84	0.03	30.0	8.0	/	/	70.0	1.2	18.0	0.8
MT-18C	4.0	0.5	2.79	0.03	30.0	8.0	/	/	69.0	1.2	18.0	0.8

Преимущества углеродистого магнезиального кирпича

1.Excellent High Temperature Resistance
2.Corrosion Resistance
3.Good Thermal Shock Resistance
4.Good Thermal Conductivity

Применение углеродистого магнезиального кирпича

Magnesia carbon bricks are mainly used in the lining of converters, AC electric arc furnaces, DC electric arc furnaces, and slag lines of ladles in the steelmaking industry.