Cordierite Mullite Kiln Shelves
- Bulk Density/g·cm3: ≥1.85
- Apparent Porosity/%: 26士4
- Room Temperature Flexural Strength/MPa: ≥10
- High Temperature Flexural Strength (1250℃*0.5h)/MPa: ≥9
- Thermal Expansion Coefficient (20℃~1000℃)/10-6 ℃-1: ≤2.8
- 인증 ISO9001/ISO14001/ISO45001/ISO50001
- Processing Service: Bending, Welding, Punching, Decoiling, Cutting, Moulding
Description of Cordierite Mullite Kiln Shelves
Cordierite-Mullite kiln furniture is composed of cordierite, mullite and glass phase. Due to the high temperature resistance of mullite and the low expansion of cordierite, Cordierite-Mullite kiln furniture has excellent thermal shock resistance,long service time,can be safety used at temperature below 1350℃.
Kerui Cordierite Mullite Kiln Shelves Technique Data
| 아이템/등급 | CMG1 | CMG2 | CMD1 | CMD2 |
|---|---|---|---|---|
| Bulk Density/g·cm3 | ≥1.85 | |||
| 겉보기 다공성/% | 26士4 | |||
| Room Temperature Flexural Strength/MPa | ≥10 | |||
| High Temperature Flexural Strength (1250℃*0.5h)/MPa | ≥12 | ≥9 | ||
| Thermal Expansion Coefficient (20℃~1000℃)/10-6 ℃-1 | ≤2.8 | ≤3.8 | ≤2.8 | ≤3.8 |
| Thermal Shock Resistance (1100℃, Water Cooling)/Timeresistance | ≥30 | |||
Regular dimension (mm):
600*500 600*470 600*400 500*500 500*370 500*340 500*450 485*460 450*450 450*420 420*380 360*360 340*340 330*330 320*320 310*310
Note: Thickness on customer’s requirement
The specific types of cordierite mullite kiln furniture we can provide are as follows. If you have any questions or needs, please contact us to obtain the latest information and the best quotation!
Features of Cordierite Mullite Kiln Furniture
1. Good thermal conductivity
2. Good high temperature strength
3. Wear resistant and erosion resistant
4. Good thermal shock resistance
5. Good corrosion resistance
6. Good oxidation resistance
Application of Cordierite Mullite Kiln Furniture
Cordierite Mullite kiln furniture is mainly used in ceramic shuttle kiln, tunnel kiln,roller kiln for firing sanitary ware,electrical ceramics ,crystallized glass panesl,hard ferrites,powder metallurgy,stoneware,earthenware,redware,porcelain,bone china,pottery pot,dolomitic pottery,heavy clays.