| 항목 | KR-AZS41 | KR-AZS36 | KR-AZS33 |
|---|---|---|---|
| SiO2, % | 12 | 13 | 15 |
| Al2O3, % | 45 | 49 | 50 |
| ZrO2, % | 40.5 | 35.5 | 32.5 |
| 벌크 밀도, g/cm3 | 4.05 | 3.9 | 3.8 |
| 겉보기 다공성, % | 0.6 | 0.8 | 0.7 |
| 유리체의 초기 침전 온도, ℃ | 1400 | 1400 | 1400 |
| 유리체상 삼출, % (1500℃*4h) | 1.5 | 2.3 | 2 |
| 정적 조건에서의 용융 유리 침식 방지 속도, mm/24시간 (1500℃*36시간, 일반 소다 석회 유리) | 1.2 | 1.3 | 1.4 |
| 버블 방출 속도, % (1300℃*10시간, 일반 소다 석회 유리) | 0.6 | 1 | 1.2 |
Fused bricks, also known as fused zirconia corundum bricks, are abbreviated as AZS, which are arranged in the order of their content according to the three chemical components of the Al2O3-ZrO2-SiO2 ternary system phase diagram. AZS is abbreviated from “A” of Al2O3, “Z” of ZrO2 and “S” of SiO2, according to JC/T industry standard.For example, No. 33 fused zirconia corundum refractory brick is referred to as “AZS-33#”, No. 36 fused zirconia corundum refractory brick is referred to as “AZS-36#”, and No. 41 fused cast zirconia corundum refractory brick is referred to as “AZS-41#” .
1.Extremely High Temperature Resistance
2.Excellent Corrosion Resistance
3.High Softening Temperature under Load
4.Strong Slag Resistance
5.High Strength and Wear Resistance
6.Excellent Thermal Shock Stability
7.Low Permeability
AZS-33은 액체 유리에 대한 내식성이 우수하고 돌이나 기타 결함이 발생하기 쉽지 않으며 작은 기포가 발생할 가능성이 낮습니다. 따라서 AZS-33 벽돌은 유리 가마에서 널리 사용되며 주로 용융 풀의 상부 구조, 풀 벽 벽돌 및 작업 풀의 포장 벽돌 및 재료 채널에 적용 할 수 있습니다.
AZS36 벽돌은 AZS33 벽돌과 동일한 공융체를 가질 뿐만 아니라 더 많은 연동 지르코니아 결정의 증가와 유리 상 함량의 감소로 인해 용융 풀 벽 벽돌, 포장 벽돌, 충전 포트 벽돌 등과 같이 액체 유리 유속이 높고 온도가 높은 영역에 적합합니다.
AZS41은 용융 및 주조 AZS 시리즈 중 가장 우수한 제품으로 액체 유리 부식에 대한 저항성이 매우 높고 유리 상 누출 온도가 매우 높습니다. 그것은 탱크 벽, 공급 입구 코너, 흐름 구멍, 가마 능선, 탱크 바닥 버블 링 및 유리 용광로의 핫스팟에있는 모든 전기 용해로와 같은 주요 부품에 널리 사용됩니다.