High alumina cement (formerly known as bauxite cement) is a hydraulic cementitious material with aluminate as the main mineral component, which is prepared by bauxite and lime in a certain proportion, calcined and ground, also known as aluminate cement.
| Articolo/Grado | CA50 | CA70 | CA80 | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
| Composizione chimica | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
| ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
| ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| Finezza | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
| -45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
| Tempo di impostazione | Tempo di impostazione iniziale (min) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
| Tempo di indurimento finale (min) | ≤360 | ≤360 | ≤360 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
| Resistenza (ISO) | Resistenza alla flessione/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
| 72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
| Resistenza alla compressione/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
| 72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
| 325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
| Aree superficiali specifiche ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / | ||
In addition, we also supply: CA40/41 Cemento
1.Large Heat of Hydration
2.Strong Resistance to Sulfate Erosion
3.Good High Temperature Resistance
4.Early Strength Characteristics
1. Flues, kilns, heat treatment furnaces and other building parts 2. Blast furnaces, converters, electric furnaces, etc., can be used as lining materials 3. Lining and protection of oil refining equipment, chemical furnaces, reactors 4. Maintenance and protection of high-temperature equipment such as electric furnaces, boilers, chimneys 5. Lining and protective layer of glass melting furnaces 6. Maintenance and protection of ladles, steel ladles, steelmaking furnaces, and continuous casting equipment.
L'intero processo di consegna è tracciato e il team di esperti di Kerui risolve le esigenze specifiche del progetto con la massima professionalità. Se il progetto del cliente lo richiede, il team di esperti di Kerui si reca nel paese del cliente per fornire assistenza tecnica diretta.
Oltre alla Cina continentale, Kerui Refractory ha esportato prodotti in più di 50 Paesi e regioni in 5 continenti del mondo, tra cui Asia, Europa, America, Africa e Oceania. Abbiamo ricevuto riconoscimenti ed elogi dai clienti di tutto il mondo e riceviamo costantemente ordini di ritorno e segnalazioni da parte dei clienti.