Basic Refractory Bricks

Basic Refractory Bricks are a type of refractory material. They mainly consist of alkaline oxides like magnesia and calcium oxide. They have good resistance to high temperatures and basic slag corrosion. Widely used in steel – making furnaces, glass kilns, etc., they play a crucial role in high – temperature industrial applications. The following are several common KERUI Basic Refractory Bricks. If you have any needs, please contact us to get the best quotation!

Ladrillo de magnesia

MgO% (≥): 89-97.5
Densidad aparente (g/cm³): 2.85-3.0
Refractariedad bajo carga (℃): 1500-1700
Resistencia al aplastamiento en frío (MPa): 45-60

Ladrillo de magnesia fundida

MgO Composición química :≥95 ％;
Porosidad aparente :≤18 ％;
Resistencia al aplastamiento en frío :≥55 Mpa;
Estabilidad térmica 950℃ Ciclos de viento:≥15;

Ladrillo de carbón de magnesia

MgO%: 69-85
C%: 5-18
Densidad aparente (g/cm³): 2.79-3.05
Resistencia al aplastamiento en frío (MPa): 30-50

Ladrillo cromado Magnesia

MgO%(≥): 45-65
Cr2O3%(≥): 8-16
Porosidad aparente/%(≤): 19-21
Resistencia al aplastamiento en frío (MPa): 20-35

Ladrillo de magnesia circonio

MgO% ≥：70/75/80 ZrO2 %≥：8/10/13;
Porosidad aparente%≤：19;
Densidad aparente (g/cm3)≥：2,95;
Refractariedad bajo carga:≥1600 °C

Ladrillo de Magnesia Espinela

MgO/%(≥): 80;
Al2O3/%(≥): 10
Densidad aparente (g/cm³)(≥): 2.90
Resistencia al aplastamiento en frío(≥): 50MPa

OBTENER PRECIO