Basic Refractory Bricks are a type of refractory material. They mainly consist of alkaline oxides like magnesia and calcium oxide. They have good resistance to high temperatures and basic slag corrosion. Widely used in steel – making furnaces, glass kilns, etc., they play a crucial role in high – temperature industrial applications. The following are several common KERUI Basic Refractory Bricks. If you have any needs, please contact us to get the best quotation!
HOT
- MgO% (≥): 89-97.5
- Schüttdichte (g/cm³): 2.85-3.0
- Refraktärität unter Last (℃): 1500-1700
- Kaltstauchfestigkeit (MPa): 45-60
HOT
- MgO Chemische Zusammensetzung: ≥95 ％;
- Scheinbare Porosität :≤18 ％;
- Kaltstauchwiderstand :≥55 Mpa;
- Thermische Stabilität 950℃ Windzyklen:≥15;
HOT
- MgO%: 69-85
- C%: 5-18
- Schüttdichte (g/cm³): 2.79-3.05
- Kaltstauchfestigkeit (MPa): 30-50
HOT
- MgO%(≥): 45-65
- Cr2O3%(≥): 8-16
- Scheinbare Porosität/%(≤): 19-21
- Kaltstauchfestigkeit (MPa): 20-35
HOT
- MgO% ≥：70/75/80 ZrO2 %≥：8/10/13;
- Scheinbare Porosität%≤：19;
- Schüttdichte (g/cm3)≥：2,95;
- Feuerfestigkeit unter Last:≥1600 °C
HOT
- MgO/%(≥): 80;
- Al2O3/%(≥): 10
- Schüttdichte (g/cm³)(≥): 2.90
- Kaltstauchfestigkeit(≥): 50MPa