不定形耐火材料 热 耐火浇注料 Al2O3%: 40-95 Bulk Density: (g/cm³): 1.8-2.5 Compressive Strength: (MPa): 20-150 Max Service Temperature: (℃): 1300-1800 现在发送电子邮件 热 捣打料 Al2O3: 30-90 Bulk Density (g/cm³): 1.9-3.15 Compressive Strength (MPa): 20-100 Max Working Temperature/℃: 1400-1800 现在发送电子邮件 热 耐火泥 Al2O3%: 40-78 Fe2O3%: 0.7-1.2 Classification Temperature/℃: 1300-1600 Refractoriness Underload/℃: 1320-1600 现在发送电子邮件 热 耐火水泥 Al2O3% (≥): 50-81 Fineness(d50/μm): 5-13 Flexural Strength(72h)/Mpa: 6-12.5 Compressive Strength (72hrs)/MPa: 40-82 现在发送电子邮件 热 高铝水泥 Al2O3%: 50-81 Fineness(d50/μm): 5-13 Flexural Strength/Mpa(24h): 5.0-10.5 Compressive Strength/Mpa(24h): 30-72 现在发送电子邮件 热 铝酸钙水泥 Al2O3(%): 50-81 CaO(%): 17.5-30.5 Fineness(d50/μm): 5-13 Compressive Strength (72hrs) (MPa):40-82 现在发送电子邮件 热 低水泥浇注料 Al2O3≥/%: 45-92 SiO2≥/%: 5-50 Bulk Density (g/cm³): 2.3-3 Cold Crushing Strength/Mpa: 72-85 现在发送电子邮件 热 刚玉耐火浇注料 Al2O3 ≥/%: 80-95 Bulk Density≥/(g/cm³): 2.7-3.2 Flexural Strength ≥/MPa: 9-11 Compressive Strength ≥/MPa: 60 现在发送电子邮件 热 莫来石耐火浇注料 Al2O3≥/%: 55-70 Bulk Density≥/(g/cm³): 2.3-2.6 Flexural Strength ≥/MPa: 7-9 Max Service Temperature (℃): 1300-1500 现在发送电子邮件 热 轻质保温浇注料 Bulk Density(g/cm³): 0.5-1.8 Max. Service Temperature/℃: 1150-1350 Cold Crushing Strength(110℃*24h)≥: 1.5-20MPa Thermal Conductivity (W/m·k)350℃: 0.15-0.65 现在发送电子邮件 热 高铝耐火浇注料 Al2O3≥/%: 50-80 Bulk Density ≥/ (g/cm³): 2.15-2.65 Cold Modulus of Rupture ≥/MPa: 4-7 Cold Crushing Strength ≥/Mpa: 25-40 现在发送电子邮件 热 刚玉莫来石浇注料 Maximum Service Temperature ℃: 1550 Bulk Density(g/cm³)≥ : 2.7 1100℃ Cold Crushing Strength(Mpa) ≥ : 100 Linear Dimensional Change % ≤ : -0.3 现在发送电子邮件 热 耐酸浇注料 SiO2% (≥): 45-52 Bulk Density (g/cm³): 1.6-2 Acid Resistance% (≥): 95 Cold Crushing Strength (MPa): 5-10 现在发送电子邮件 热 耐磨铸件 Al2O3≥/%: 70-85 Bulk Density ≥/ (g/cm³): 2.8-3.1 High strength and wear resistance High density, low porosity 现在发送电子邮件 热 碳化硅浇注料 SiC+C≥/%: 58-83 Good resistance to erosion Abrasiveness resistance For cement kiln, EAF and steel ladel 现在发送电子邮件 热 超低水泥浇注料 Al2O3 ≥/%: 45-95 Cao≥/%: 1.15 Bulk Density (g/cm3) ≥2.35-3.2 Refractoriness ≥1710-1790℃ 现在发送电子邮件 热 钢纤维浇注 Al2O3 ≥/%: 70-80 Better thermal shock resistance Used in building material industry 样品：可进行样品测试 现在发送电子邮件 热 塑料耐火材料 Plasticity Index%：12-35 Al2O3% (≥)：35-80 Bulk Density (g/cm³)：2.15-2.65 Compressive Strength (Mpa)：6.0-8.0 现在发送电子邮件 热 Gunning Mix Al2O3% (≥): 32-70 Fe2O3% (≥): 1.1-4.5 Type：Dense Gunning Material Shelf Life (months)：9 现在发送电子邮件 热 耐酸砂浆 Strong Acid Resistance Good Adhesion High Sealing Performance Good Heat Resistance 现在发送电子邮件 联系我们 请在右边的表格中填写您的询问。我们将在 6 小时内给您答复。 电子邮件： market@keruiref.com 电话/whatsapp： +86 19138178880 制造基地： 超化耐火材料工业区、 中国河南省新密市 * 名称： * 电子邮件 电话/微信 国家： * 信息：