High alumina cement (formerly known as bauxite cement) is a hydraulic cementitious material with aluminate as the main mineral component, which is prepared by bauxite and lime in a certain proportion, calcined and ground, also known as aluminate cement.
| Ürün / Sınıf | CA50 | CA70 | CA80 | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
| Kimyasal Bileşim | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
| ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
| ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| İncelik | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
| -45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
| Ayar Zamanı | İlk Ayar Süresi (dak) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
| Son Priz Süresi (dak) | ≤360 | ≤360 | ≤360 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
| Güç (ISO) | Eğilme Dayanımı/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
| 72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
| Basınç Dayanımı/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
| 72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
| 325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
| Özgül Yüzey Alanları ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / | ||
In addition, we also supply: CA40/41 Çimento
1.Large Heat of Hydration
2.Strong Resistance to Sulfate Erosion
3.Good High Temperature Resistance
4.Early Strength Characteristics
1. Flues, kilns, heat treatment furnaces and other building parts
2. Blast furnaces, converters, electric furnaces, etc., can be used as lining materials
3. Lining and protection of oil refining equipment, chemical furnaces, reactors
4. Maintenance and protection of high-temperature equipment such as electric furnaces, boilers, chimneys
5. Lining and protective layer of glass melting furnaces
6. Maintenance and protection of ladles, steel ladles, steelmaking furnaces, and continuous casting equipment.
Tüm teslimat süreci takip edilir ve Kerui'nin uzman ekibi belirli proje ihtiyaçlarını en üst düzeyde profesyonellikle çözer. Müşterinin projesi gerektiriyorsa, Kerui'nin uzman ekibi yüz yüze teknik destek sağlamak için müşterinin ülkesine gidecektir.
Kerui Refrakter, Çin anakarasının yanı sıra Asya, Avrupa, Amerika, Afrika ve Okyanusya dahil olmak üzere dünyanın 5 kıtasında 50'den fazla ülke ve bölgeye ürün ihraç etmiştir. Dünyanın her yerindeki müşterilerimizden takdir ve yüksek övgü aldık ve sürekli olarak müşterilerin iade siparişlerini ve yönlendirmelerini alıyoruz.