Tijolo refratário de sílica

Description of Silica Fire Brick

Refractory silica brick is an acid refractory material mainly composed of tridymite, cristobalite and a small amount of residual quartz and glass phase. The silica content is above 94%. The true density is 2.35g/cm3. It has anti-acid slag corrosion performance. Higher high temperature strength. The temperature of softening under load is 1620～1670℃. Long-term use at high temperature without deformation. Low thermal shock stability (heat exchange in water is 1~4 times). Natural silica is used as raw material, and an appropriate amount of mineralizer is added to promote the conversion of quartz in the green body to tridymite. Slowly fired at 1350-1430°C under reducing atmosphere. When heated to 1450°C, there will be about 1.5~2.2% of the total volume expansion, and this residual expansion will make the cuts close together, ensuring good air tightness and structural strength of the masonry.

OBTER PREÇO

KERUI Silica Fire Brick Technique Data Sheet

Item/Grau		GZ-94
ω (SiO2)/%	μ0	≥94
	σ	1.0
ω (Fe2O3)/%	μ0	≤1.4
	σ	0.3
Porosidade aparente/%	μ0	≤24
	σ	1.5
True Density (g/cm³)	μ0	≤2.35
	σ	0.1
Resistência ao esmagamento a frio/MPa	μ0	≥30
	σ	10
	Xmin	20
0.2MPa Subcarga de refratariedade/℃	μ0	≥1650
	σ	13

Advantages of Silica Fire Brick

Resistência a altas temperaturas

The refractoriness of silica bricks is 1690℃ to 1730℃. It can maintain the stability and integrity of the structure at high temperature.

Excelente condutividade térmica

Refractory silica bricks have good thermal conductivity, and the load softening temperature is high, generally above 1620℃, which is only 70-80℃ lower than its refractoriness. The thermal conductivity of silica bricks increases with increasing operating temperature without residual shrinkage.

Excelente resistência à corrosão

Silica brick is an acid refractory material, which has good resistance to acid slag erosion, and has high corrosion resistance to acids, alkalis, solution and other chemical substances.

Estabilidade dimensional

Refractory silica bricks have a low thermal expansion coefficient, so the dimensional change is small under high temperature environment.

Customizability

Refractory silica bricks can be customized according to different needs, including size, shape and refractory grade.

Application of Silica Fire Brick

Indústria metalúrgica

Refractory silica bricks are widely used in high-temperature smelting equipment such as blast furnaces, steelmaking furnaces, ironmaking furnaces, electric furnaces and molten iron treatment equipment in the metallurgical industry.

Indústria química

Refractory silica bricks are used in high temperature reaction furnaces, kilns, reforming furnaces, heating furnaces, heat exchangers and grates in the chemical industry.

Indústria da energia eléctrica

Refractory silica bricks are widely used in the electric power industry for high-temperature equipment such as combustion furnaces, boilers, chimneys, and thermal power stations.

Glass and Ceramic Industry

Refractory silica bricks are used in glass and ceramic industries for equipment such as glass melting furnaces, kilns and kiln furniture. Because of their high heat resistance, they can withstand the melting process of high-temperature glass and ceramic materials, ensuring product quality and production efficiency.

Indústria do ferro e do aço

Refractory silica bricks are widely used in the iron and steel industry for equipment such as ladles, iron gates, sprue and molten iron wells. They can withstand the impact and corrosion of high-temperature molten steel, protecting the durability and production efficiency of equipment.