High alumina cement (formerly known as bauxite cement) is a hydraulic cementitious material with aluminate as the main mineral component, which is prepared by bauxite and lime in a certain proportion, calcined and ground, also known as aluminate cement.
| Item/Grau | CA50 | CA70 | CA80 | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| A600 | A700 | A900 | CA70 | CA70W | CA70S | CA71 | CA80 | CA80S | |||
| Composição química | ω (SiO2) ≤/% | 7.8 | 7.5 | 5.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | |
| ω (Al2O3)/% | 50.0 | 51.0 | 53.5 | 68.5-70.5 | 68.5-70.5 | 68.5-70.5 | 69.5-71.5 | 78.0-81.0 | 78.0-81.0 | ||
| ω (Fe2O3) ≤/% | 2.5 | 2.5 | 2.5 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | ||
| ω (CaO)/% | / | / | / | 28.5-30.5 | 28.5-30.5 | 28.5-30.5 | 27.5-29.5 | 17.5-20.5 | 17.5-20.5 | ||
| ω (MgO) ≤/% | / | / | / | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (R2O) ≤/% | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | ||
| ω (S) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| ω (Cl) ≤/% | 0.1 | 0.1 | 0.1 | / | / | / | / | / | / | ||
| Finura | d50/μm | / | / | / | 11-4 | 8-11 | 6-9 | 10-13 | 5-8 | 5-8 | |
| -45μm ≤/% | / | / | / | 8.0 | 5.0 | 5.0 | 8.0 | 5.0 | 5.0 | ||
| Tempo de definição | Tempo de configuração inicial (min) | ≥45 | ≥60 | ≥90 | 120-180 | 30-90 | 180-240 | 150-210 | 30-90 | 90-150 | |
| Tempo de endurecimento final (min) | ≤360 | ≤360 | ≤360 | 150-240 | 90-180 | 240-330 | 210-300 | 90-180 | 270-360 | ||
| Resistência (ISO) | Resistência à flexão/Mpa | 24h | 6.0 | 6.5 | 8.0 | 7.5-10.0 | 8.0-10.5 | 8.0-10.5 | 8.5-11.0 | 5.0-7.5 | 5.0-7.5 |
| 72h | 7.0 | 7.5 | 10.0 | 10.0-12.0 | 10.5-12.5 | 10.5-12.5 | 11.0-12.5 | 6.0-8.5 | 6.0-8.5 | ||
| Resistência à compressão/Mpa | 24h | 45 | 55 | 72 | 40-50 | 45-55 | 45-55 | 50-60 | 30-40 | 30-40 | |
| 72h | 55 | 65 | 82 | 45-55 | 50-60 | 50-60 | 55-65 | 40-50 | 40-50 | ||
| 325M ≤/% | 15 | 12 | 8 | / | / | / | / | / | / | ||
| Áreas de superfície específicas ≥/ (㎡/kg) | 300 | 320 | 350 | / | / | / | / | / | / | ||
In addition, we also supply: Cimento CA40/41
1.Large Heat of Hydration
2.Strong Resistance to Sulfate Erosion
3.Good High Temperature Resistance
4.Early Strength Characteristics
1. Flues, kilns, heat treatment furnaces and other building parts 2. Blast furnaces, converters, electric furnaces, etc., can be used as lining materials 3. Lining and protection of oil refining equipment, chemical furnaces, reactors 4. Maintenance and protection of high-temperature equipment such as electric furnaces, boilers, chimneys 5. Lining and protective layer of glass melting furnaces 6. Maintenance and protection of ladles, steel ladles, steelmaking furnaces, and continuous casting equipment.
Todo o processo de entrega é acompanhado e a equipa de especialistas da Kerui resolve as necessidades específicas do projeto com o máximo profissionalismo. Se o projeto do cliente o exigir, a equipa de especialistas da Kerui desloca-se ao país do cliente para prestar assistência técnica presencial.
Além da China continental, Kerui Refractory exportou produtos para mais de 50 países e regiões em 5 continentes em todo o mundo, incluindo Ásia, Europa, América, África e Oceania. Recebemos reconhecimento e elogios de clientes em todo o mundo, e estamos constantemente a receber pedidos de retorno e referências de clientes.